Uses:it has good stability, good solvent releasing capacity, and good resistant to bending, good glossiness, good adhesive force and good resistance to gel. It can be used in printing industry to produce solvent type printing ink for soft plate, surface printing ink for plastic and hot-melt adhesive.
Performance:it has strong adhesive force, good resistant to bending, good resistant to water and excellent stability. It can work well with nitro fiber. It can work with pigment and filler to offer bright and brilliant colors.
Itemindex
Benzene soluble polyamide resinsalcohol soluble polyamide resins
Hj-7010hj-1014hj-1417hj-1720hj-9088lhj-9088hj-9088hhj-0005hj-2000hj-2003
Acid value mgkoh/g <5555555555
Amine value, mgkoh/g <5555555555
Viscosity, mpa.S70~100100~140140~170170~20080~120120~160160~20080~160120~17080~160
Softening point oc105~118105~118105~118105~118105~118105~118105~11895~105115~125110~120
Chroma, <8888888888
Solubilityall
Note: for benzene soluble polyamide resin: the inspection conditions of viscosity & chroma: solid is 40%, solvents are xylene/ isopropanol/ absolute alcohol (4:3:3), viscosity method is rotation method. For solubility: the solution is 40% of resin solution, the ratio just like viscosity inspection.
For alcohol soluble polyamide resin: the inspection conditions of viscosity & chroma: solid is 50%, solvent is 95% ethanol, rotation method (hj-2000); the inspection conditions of viscosity & chroma: solid is 40%, solvents are isopropanol/absolute alcohol/normal butyl alcohol (1:1:1), rotation method (hj-2003). For solubility: the solution is 40% of resin solution, the ratio just like viscosity inspection.
HT-65 high molecular weight polyamide resin especially designed for hot melt-adhesive use.
This resin has the characteristics of high softening point, and high molten viscosity so
that it is suitable for applications where high heat resistance, high creep strength, high adhesive
strength required and it is especially application for low pressure moulding.
PA66 GF33 material can be used for Electric cooker, soybean milk and juice maker and other home appliances, air conditions shell, car accessories, fan heater, instrument panel, thermal jug...
New Energy vehicle charging pile and charging gun, automotive, MCB, appliance parts, low temperature resistant nylon tie band, power tools, office chair base, hydrant handle, ski equipment components, breaker, connector...
Battery cell jar case, heating appliances case, panel, plug, electronic shell, instrument frame, auto parts and etc...
HT-45 is a high molecular weight polyamide resin especially
designed for hot melt adhesive use. It is easy to soluble in mixed organic
solvent , such as aliphatic or aromatic hydrocarbons and alcohols type solvent.
This resin has the characteristics of good mechanical strength, heat resistance, flexibility
and long open times(good workability).
This product is suitable for bonds to many difficult substrates including : PCB parts, metals, plastics, leather and fabric.
The co-solvent polyamide resin mainly used in gravure printing ink, plastic surface printing inks and hot melt adhesives.The alcohol polyamide resin mainly used in flexographic printing inks, gravure printing inks.Both of them are used in over-printing varnish.
21045 Polyamide Resin Suppliers
Short on time? Let Polyamide Resin sellers contact you.
Properties: low freezing point co-soluble polyamide resin, which has well cold resisting property and indoor temperature turn frost compared with same kind of resin, which has good adhesion, excellent compatibility, good stability and high glossiness.
Major technical index:
ItemUnitIndexTest method
Acid valueMgkoh/g 5Titrimetry
Amine valueMgkoh/g 4Titrimetry
Softening point 105±5Ring-ball
ViscosityMpa.S/25 90-160Rotary viscosimetry
Mixing proportion:40%resin, 60%solvent
(xylene:ipa:ethanol=4:3:3)
Color Size 7Fe-co colorimetry
Freezing point -5±5Freezing point instrument.
Packing, transportation and storage:
Paper-plastic bag, 25kg/bag.
Attention should be paid to damp proof and high temperature. It is generally stored in the
Cool and dry ventilated places, and high temperature, solarizing and drenching are forbidden
In the course of transporting.
Glossiness, good adhesive force and good resistance to gel. It can be used in printing industry to produce solvent type printing ink for soft plate, surface printing ink for plastic and hot-melting adhesive.
Performance: it has good adhesive force, good resistant to bending, good resistant to water and good stability. It can work well with nitro fiber. It can work with pigment and filler to offer bright and brilliant colors.
A high molecular weight polyamide resin especially designed for hot melt adhesive use.
It is easy to soluble in mixed organic solvent such as aliphatic or aromatic hydrocarbons and alcohols type solvent. This resin has the characteristics of good mechanical strength heat resistance, flexibility and long open times(good workability) .
A high viscosity, reactive polyamide resin designed for use with liquid epoxy resins to achieve cure at room temperature.
It is suitable for use in adhesives, civil engineerings, high solids anti-corrosive coatings for marine and maintenance coatings where excellent adhesion, good flexibility and toughness, good water and corrosion resistance are required.
Polyamide resin green speciality chemicals companies Eco-Resin green chemical supply
Description
Polyamide produce from the reaction of dimerised and trimerised fatty acid with polyamines.
Polyamide resin Advantage
Non-toxic and harmless, no sulfur, no aromatics, no benzene, no heavy metals, easy degradation, no residue. It is an environmentally friendly green organic intermediate.
Eco-Resin Technical index
Item Unit SJ-PA299 SJ-PA3D99 SJ-PA3AN99
Soften point 112 112.5 104
Color(Fe-Co) Gardner 6 6 6
Acid value mgKOH/g 5.1 5.2 2.8
Amine value mgKOH/g 3.4 3.0 1.4
Viscosity Pa.s/25 90 130 130
Freezing point 4 3 -1.5
Application
Polyamides are versatile curing agents for epoxies. They are pleasant to handle, are compatible with many resins, and their mixing ratio with resin are not critical. Fairly long pot life is possible. It yields casting with good impact strength. Excellent adhesion to many different substrates. Sometime polyamides are regarded as flexibilizers as well as curing agent. Polyamide Adducts provide good compatibility and better cure under adverse conditions than standard polyamides without induction time.
Pure Himalayan Power -Shilajit Resin
Sourced from the heights of the Indian Himalayas, our 100% Pure Shilajit Resin is a natural vitality booster trusted for centuries.
Nitrogen - 46% min
Moisture - 1% max
Biuret - 1% max
Prilled - 0.85-2mm
Granular - 2-4mm 90-94%min
color - Pure White
Radiation - Non-Radiactive
Free Ammonia - 160pxt ppm max
Character
Nontoxic, nonirritating, high flash point and fire point not freeze under low temperature, good viscosity and good congluti-nation. It dissolves in the majority of solvents, never dissolve in the water.
Application
Dimer acid and amine will react to produce much different molecular weight polyamide resin. Mainly used to make graver?or flexo?printing ink, epoxy paint, the curing agent and the epoxy cementing material, lubricant .Dimer acid is used to make hot melt adhesive, which is widely used to make thermoplastic product and joint of electric cable in the posts and telecommunications, the communication equipment.