Size : 6.6mm-8.5mm
Protein: 42%
Moisture : 13-15%
Admixture : 0.01%
Geminatiom : 97%
Average Protein 35%, minimum
Maximum Moisture Content : 14%
Splits : 11% maximum
Foreign matters : 2% maximum
Soybeans, other color : 2% maximum
Hear damaged kernels : 0.5% maximum
Total damaged kernels : 3.0% maximum
Oil Content : 18.5% plus or minus 0.5%
Size : 6.6mm-8.5mm
Protein : 42%
Moisture : 13-15%
Admixture : 0.01%
Geminatiom : 97%
Average Protein 35%, minimum
Maximum Moisture Content : 14%
Splits : 11% maximum
Foreign matters : 2% maximum
Soybeans, other color : 2% maximum
Hear damaged kernels : 0.5% maximum
Total damaged kernels : 3.0% maximum
Oil Content: 18.5% plus or minus 0.5%
Icumsa : 45 Rbu Icumsa
Ash Content : 0.04% Maximum By Weight
Moisture : 0.04% Maximum By Weight
Magnetic Particles : Mg/kg 4
Solubility : 100% Dry & Free Flowing
Granulation : Fine Standard
Polarization : 99.80 Minimum
Max As : 1 P.p.m.
Max Os : 2 P.p.m.
Max Cu : 3 P.p.m.
Colour : Sparkling White
Sediments : None
So : Mg/kg 20
Reducing Sugar : 0.010% Maximum In Dry Mass
Radiation : Normal W/o Presence Of Cesium Or Iodine So2: Certified
Substance : Solid, Crystal
Smell : Free Of Any Smell
Hpn Staph Aureus : Per 1 Gram Nil
Microbiological Limits : Pathogenic Bacteria Including Salmonella Per 1 Gram Nil Bacillus Per 1 Gram Nil
Pesticide Traces : Maximum Mg/kg Basis Ddt 0.005 Photoxin 0.01 Hexachloran Gamma Isomer 0.005
Crop: recent Crop Or Proceeding
Phytosanitary Certificate Of No Radiation, No Virus, No Insect Parts, No Rodent Excrement, No Husks And No Poisonous Matter. Product Is Suitable For Human Consumption
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Tests Value Unit
Melt Flow Rate (MFR) 3.2 g/10min
Density 0.939 g/cm3
Melting Point 127 C
Tensile Yield Strength 21 Mpa
Tensile Strength at Break 28 Mpa
Elongation at Break 1,100 %
Flexural Modulus 750 Mpa
Brittle Temperature <-60 C
Tests Value Unit
Melt Flow Rate (MFR) 20 g/10min
Density 0.924 g/cm3
Tensile Strength MD12 Mpa
TD 10
Elongation at Yield 13 %
Elongation at Break 200 %
Dark Drop Impact 105 g
Brittle Temperature(F 50) -70 C
Vicat Softening Point 90 C
Tests Value Unit
Melt Flow Rate (MFR) 20 g/10min
Density 0.924 g/cm3
Tensile Strength MD12 Mpa
TD 10
Elongation at Yield 13 %
Elongation at Break 200 %
Dark Drop Impact 105 g
Brittle Temperature(F 50) -70 C
Vicat Softening Point 90 C