Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50°C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 °C
Blowing molding Grade HDPE
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190°C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Item Test Condition Test Method Value Unit
Density ISO 1183 0.950~0.955 g/cm
MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield ISO 527-2 24 MPa
Elongation at break ISO 527-2 >600 %
Low density polyethylene (LDPE), also known as high pressure polyethylene, is a kind of plastic material, it is suitable for thermoplastic molding processing of various forming processes, forming processing is good. LDPE is mainly used for thin film products, but also for injection products, medical devices, medicine and food packaging materials, blow molding hollow molding products and so on.
Item
LDPE Granules
Low-density polyethylene (LDPE) is a synthetic resin using a high-pressure process via free radical polymerization of ethylene and is therefore also called high-pressure polyethyleneâ. It features light, flexible, good freezing resistance and impact resistance. LDPE is chemically stable. It has good resistance to acids (except strongly oxidizing acids), alkali, salt, and excellent electrical insulation properties. Its vapor penetration rate is low.