Soundness in microstructures with homogeneous composition, littlegregation and lower MgO content. Stable and even lasting with high absorption of Mg.Much smaller and globular graphite and high nodularization efficiency when treated.
Nodularization temperature is recommended at 1400-1450 when melted from a cuppola,or at 1450-1500 when from an electric furnace. Added at 1.5%-1.6% when sulphur in the liquid cast iron is as high as 0.065-0.09%, or 1.4%-1.5% when sulphur is as high as 0.05-0.065%.
Supplied in the form of grain(5-25mm) or following special requirement. Packed in plastic braids with inner wet resistant plastic film. Per packed parcel is 25kg n.m.
Model Chemical Composition%
Si Mg Ca Re Ba La Fe
BN-126 38-44 6-7.5 1.0-3.0 1.8-2.5 - balance
BN-127 38-44 6.3-7.5 2.0-3.5 2.5-4.0 1.2-2.0 balance
BN-137 38-44 6.3-7.5 1.0-3.0 2.5-4.0 - balance
BN-138 38-44 7.0-9.0 2.0-3.0 2.0-4.0 - balance
BN-158 38-44 7.0-9.0 2.0-3.0 4.0-6.0 - balance
BN-101 44-48 5.6-6.5 0.8-1.2 - ï¼?2.0 proper balance
BN-104 44-48 5.5-6.5 1.0-1.5 0.4-0.6 proper balance
Standard Size: 0.6-6mm,1-12mm,5-25mm,4-30mm
Packing: 25kg woven plastic bag in 1mt jumbo bag.
Note: Chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements.
Characteristics
1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed.
2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products.
3.High mechanical strength and strong deoxygenation and desulfuration effects.
Characteristics
1.Ferro Silicon Magnesium Alloy is shaped in gray lump with metal luster. It is solid and brittle so that it is easy to be smashed.
2.With stable reaction, the absorption rate of Mg. will be increased which is helpful for getting high-quality casting products.
3.High mechanical strength and strong deoxygenation and desulfuration effects.
Trade markCodeChemical composition%Melting methodApplication range
MgReSiCaAlTiFe
Fesimg5re25-24.0-6.01.0-3.038-442.0-3.01.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg6re16-15.0-7.00.5-1.538-442.0-3.01.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg7re17-16.0-8.00.5-1.538-441.0-1.51.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg7re37-36.0-8.02.0-4.038-442.0-3.51.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg8re37-37.0-9.02.0-4.038-442.0-3.51.00.5RestElectric furnace or cupolaAll kinds of
Di casting
Fesimg8re58-57.0-9.04.0-6.038-442.0-3.51.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg8re78-77.0-9.06.0-8.038-442.0-3.51.00.5RestElectric furnaceAll kinds of
Di casting
Fesimg10re710-79.0-11.06.0-8.038-442.0-3.51.00.5RestElectric furnaceAll kinds of
Di casting
Mainly used in automobile industry, mechanical casting, ductile iron pipes and other metallurgical industry.The addition of magnesium (mg) causes spheroidal graphite to grow.
Packing: 25kg woven plastic bag in 1mt big bag
Note: chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements.
Des. Casted parts/components
Cast method Sand cast, die cast, Lost foam/wax, investment casting, centrifugal casting,
Processing Precision CNC machining, grinding, tapping ,painting and assembly
Finish treatment Tempering , quenching, annealing, normalizing
Surface treatment -blast shooting
-HDG,zince
-Chrome plating
-Powder coating
-Anodizing
-Polishing
-Electrophoresis
-Electrostatic color paining
QA Caliper, roughness tester, strength tester, spectrograph, CMM, metalloscope and etc.. 3party inspection report is able to serve as your needs.
Material range Die casting: Aluminum or alloy A360, A380, A390, ADC12,ADC10,ALSI09 etc.
Ductile iron casting part: QT400 , QT450, QT500, QT550, QT600, QT700
Zinc & Zinc alloy. ZA-3,ZA-5,ZA-8
Sand casting:ZL101,ZL104,ZL102 and so on.
Iron casting: HT150, HT200, HT250, HT300,etc.
Standard: JIS, DIN, ASTM,BS, ISO,AISI
Application scope -Woodworking hand tools,
-Electrical high voltage fittings,
-Cookware, BBQ grill,
-Pump/valve body or accessories ,
-Drainage grate,
-Construction accessories
Package Standard seaworthy packing
FOB Port CN DLC
Standard ISO,GB,ASTM,BS,JIS,AISI,DIN and etc.
1. The property of company is OEM or trading business only? Where is the location of foundry?
- More than decade experiences both on manufacturing and exporting of alloy castings.
- The foundry , CNC workshop and assembly line are in Province Liaoning, construction area occupied total 20000m2.
2. The way to obtain the quotation.
-We r always standby, the more accuracy parameters you provided, the more close price you will be obtained. The drawing in AUTOCAD, PROE,SOLIDWORKS and etc. what the general formats are preferred to.
3. Leading time, MOQ and delivery term.
- Leading time or MOQ depends on the complexity ,casting structure and dimension. Any requirements could settle by mutual negotiating. for the Shipping transportation , the world top 10 ocean carriage brands for transporting period could be referred to . FOB ,CIF, CFR what types stipulated in incoterms 2010 are acceptable.
For more just call or write to me with undersigned.
a. Price of product - depends on customers product
b. Product origin - Turkey
c. Key Specifications/Special Features
d. Minimum Order Size : 1 full Truck or 1 full container
e. Packaging Details: Euro pallets- Wooden boxes or other customer-specific packaging details.
Pearlitic rolls are composed by nodular graphite and carbides arranged in a pearlitic matrix. It's properties are similar to Indefinite Chill except that the graphite structure is changed from flake to spheroidal forms. Pearlitic rolls will have higher strength than Indefinite Chill. Pearlitic roll can be produced by static casting (Monoblock) or by using the centrifugal cast (CC) Double-pour method.
Fesimg(nodulizer)
1: re 0.8-1.2% mg 4.2-4.7% ca 1.5-2.0% si 45-50% al<2.0% 2: re 0.8-1.2% mg 6.0-6.5% ca 0.8-1.2% si 44-48% al<2.0% 3: re 1.0-1.5% mg 5.0-5.5% ca 2.0-2.5% si 45-50% al<2.0% 4: re 1.0-1.5% mg 5.7-6.2% ca 1.7-2.2% si 42-45% al<2.0% 5: re 1.5-2.0% mg 5.5-6.0% ca 2.0-2.5% si 45-50% al<2.0% 6: re 1.5-2.0% mg 4.5-5.0% ca 0.5-1.0% si 44-48% al<2.0% 7: re 1.8-2.2% mg 4.8-5.3% ca 1.8-2.2% si 43-47% al<2.0% 8: re 1.8-2.2% mg 5.0-5.5% ca 1.5-2.0% si 43-47% al<2.0% 9: re 1.9-2.3% mg 5.3-5.8% ca 2.2-2.6% si 44-48% al<2.0% 10: re 2.0-2.5% mg 6.0-6.5% ca 2.0-2.5% si 44-48% al<2.0% 11: re 2.0-2.5% mg 7.0-8.0% ca 2.0-2.5% si 44-48% al<2.0%standard size: 2-12mm; 5-15mm; 5-25mm; 10-30mm standard packing: 25kgs plastic woven bag.
All the composition of each element, other special elements do not be mentioned above, size and packing can be changed upon request.
Trade markChemical composition%
ReCe/reMgCaSiMnTiMgoFe
Not more than
195101a0.5-2.0464.5-5.51.5-3.045111Rest
195101b0.5-2.0465.5-6.51.5-3.045111Rest
195101c0.5-2.0466.5-7.51.0-2.545111Rest
195101d0.5-2.0467.5-8.51.0-2.545111Rest
195103a2.0-4.0466.0-8.01.0-2.045111Rest
195103b2.0-4.0466.0-8.02.0-3.545111Rest
195103c2.0-4.0467.0-9.01.0-2.045111Rest
195103d2.0-4.0467.0-9.02.0-3.545111Rest
195105a4.0-6.0467.0-9.01.0-2.044211.2Rest
195105b4.0-6.0467.0-9.02.0-3.044211.2Rest
195107a6.0-8.0467.0-9.01.0-2.044211.2Rest
195107b6.0-8.0467.0-9.02.0-3.044211.2Rest
195107c6.0-8.0469.0-11.01.0-3.044211.2Rest
1951098.0-10.0468.0-10.01.0-3.044211.2Rest
19511817-20467.0-10.01.5-3.542221.2Rest
Rare-earth ferro silicon magnesium alloy is lump in shape with metal luster. It is solid and brittle so that it is easy to smash, and it glisten with blue luster from silver gray body.
Packing: 25kg woven plastic bag in 1mt big bag
Note: chemical composition, size and packing of above mentioned products can be adjusted according to customer's requirements.
Cast Iron and Ductile Iron tube and fittings PL739
Cast Iron and Ductile Iron tube and fittings can be offered by our comapny to meet different engineering needs.
The difference between ductile iron and gray iron
1. Different chemical composition
Nodular cast iron contains nodular graphite, which can improve its toughness and strength, while reducing brittleness. Gray cast iron contains a lot of carbon, so that its hardness and wear resistance is high, but the toughness is poor.
2. Different organizational structures
The structure of nodular cast iron contains nodular and ferrite, and the distribution of nodular is uniform. While the structure of gray cast iron is mainly ferrite and pearlite, and the distribution of pearlite is uneven.
3. Different performance
Ductile iron has high strength and toughness, and has good corrosion resistance. It is uitable for the manufacture of high load and high pressure parts. The hardness and wear resistance of gray cast iron are high. It is suitable for the manufacture of friction and wear parts.
Application field
Cast iron : because of its low strength and good vibration resistance. It is often used in the production of parts under compressive stress, such as box, base, etc.
Ductile iron : because of its high strength and good toughness. It is often used in the manufacture of parts requiring high strength and toughness, such as crankshaft, connecting rod and so on.
Ramming mass is commonly used in metallurgy, building materials, non-ferrous metal smelting, chemical, machinery and other manufacturing industries.
Ramming mass is widely used in non-core intermediate frequency furnace and core induction furnace.
As an intermediate frequency furnace ramming material, refractory ramming is applied to melt gray cast iron, nodular cast iron, malleable cast iron, vermicular cast iron, and cast alloy steel; to melt carbon steel, alloy steel, high manganese steel, tool steel, heat resistant steel, stainless steel, molten aluminum and its alloys; to melt red copper, brass, white brass, bronze and its alloys, etc.
Induction furnaces are used for melting cast iron, mild steel and various alloy steels in foundries and making of steel in mini steel plants using sponge iron
The refined high silicon, low iron quartz sand and quartz powder are selected and the fused quartz sand is added as the refractory material., with no slag, no crack, damp proof, convenience of repair, and the corrosion resistance, thus greatly improving the furnace service life span and the economic benefit..
Silica ramming mass can safely be used up to an operating temperature of 1600 deg C. Since it expands very little, it is superior to both alumina and magnesia refractories to resist thermal shocks
Acid ramming material is the premixed ramming mass of the lining material. The acid ramming mass is used to smelt a series of metal materials such as ordinary steel and carbon steel.
The lining practice best suited to a particular furnace depends upon the capacity and design of the furnace, operation practice adopted during making of a heat, and furnace output.
Clinker is a nodular material produced in the kilning stage during the production of cement and is used as the binder in many cement products. The lumps or nodules of clinker are usually of diameter 3-25 mm and dark grey in color. It is produced by heating limestone and clay to the point of liquefaction at about 1400�°C-1500�°C in the rotary kiln. Clinker, when added with gypsum (to control the setting properties of cement and ensure compressive strength) and ground finely, produces cement. Clinker can be stored for long periods of time in a dry condition without degradation of quality, hence it is traded internationally and used by cement manufacturers when raw materials are found to be scarce or unavailable.
1) Standards : ISO2531, ISO4422, EN545, EN598, BS4772, AWWA C110
2) Material:GGG500-7 or Ductile iron
3) Specific types:
"T" type ductile iron pipes fittings: double socket 11.25 22.5 45 90 bend DN80-2000
-all socket tee DN80-2000
-double socket tee with flanged branch DN80-2000
-flanged socket DN80-2000
Accessories of "T" type nodular cast iron pipe fittings: Gaskets according with EPDM.
"K" type ductile cast iron pipe fittings: BOLTED GLAND BEND 90 11.25 45 22.5,CLASS K12
BOLTED GLAND CONCENTRIC TAPERS, CLASS K12
FLANGED AND BOLTED GLAND SOCKET PIECES, CLASS
BOLTED GLAND COLLARS CLASS K12
BOLTED GLAND GHANGE COLLAR CLASS K12
BOLTED GLAND TEE, CLASS K14
BOLTED GLAND SOCKET SPIGOT BEND (90 45 22.5), CLASS 12
BOLTED GLAND SOCKET SPIGOT TEE WITH FLANGED BRANCH
All above "K" type ductile iron pipe fittings specification: DN100-500
Accessories of "K" type ductile cast iron pipe fittings: Gaskets according with EPDM
Bolts & Nuts in Carbon Steel grade 4.8.
Standards : ISO 2531, ISO 4422, EN 545, EN 598, BS 4772, AWWA C110
Material : GGG500-7 or Ductile iron.