KINGMIDE 533 is fatty polyamide resin especially designed for the flexographic printing ink uses.
It is easy to alcohol soluble and mixing organic solvent -such as toluene and alcohol type solvent .
The followings are the major characteristics of the KINGMIDE 533 as used
in a flexographic printing ink formulation.
(a) good solubility into various conventional industrial solvents
(b) superior adhesion onto many kind of substrates
(c) high water resistance
(d) high gloss
KINGMIDE 550 is a solid type fatty polyamide resin synthesized
by a polycondensation of mainly the dimerized fatty acid and the alkylenepolyamines.
The major applications of KINGMIDE 550 are in the rotogravure printing inks .
KINGMIDE 550 shows superior adhesion onto wide variety of surface so that it is highly useful
for rotogravure ink formulation .
77 Aromatic Chemicals Suppliers
Short on time? Let Aromatic Chemicals sellers contact you.
HT-65 high molecular weight polyamide resin especially designed for hot melt-adhesive use.
This resin has the characteristics of high softening point, and high molten viscosity so
that it is suitable for applications where high heat resistance, high creep strength, high adhesive
strength required and it is especially application for low pressure moulding.
HT-45 is a high molecular weight polyamide resin especially
designed for hot melt adhesive use. It is easy to soluble in mixed organic
solvent , such as aliphatic or aromatic hydrocarbons and alcohols type solvent.
This resin has the characteristics of good mechanical strength, heat resistance, flexibility
and long open times(good workability).
This product is suitable for bonds to many difficult substrates including : PCB parts, metals, plastics, leather and fabric.
KINGMIDE H-120 is a high molecular weight polyamide resin especially designed for hot
melt-adhesive use.
KINGMIDE H-120 is easy to soluble in mixed organic solvent , such as
toluene and alcohol type solvent. This resin has the characteristics of high softening point, and
high molten viscosity so that it is suitable for applications were high heat resistance and high
adhesive strength and good toughness are particularly needed.
KINGMIDE H-140HP is a high molecular weight polyamide resin especially
designed for hot melt-adhesive use. It is easy to soluble in mixed organic solvent such
as toluene and alcohol type solvent. This resin has the characteristics of good
mechanical strength, good heat resistance and flexibility. It is suitable for use in
sealing and electric parts adhesive .
KINGMIDE H-170HV is a high molecular weight polyamide resin especially designed for
hot melt-adhesive use.
KINGMIDE H-170HV is easy to soluble in mixed organic solvent
suchas toluene and alcohol type solvent. This resin has the characteristics of high softening
point, and high molten viscosity so that it is suitable for applications where high heat resistance
and high adhesive strength and good toughness are particularly needed.
T-558-N is a solid-type fatty polyamide resin especially designed for HOT-MELT
STRUCTUAL ADHESIVE uses. It has superior processing properties for its ready-to-apply nature
due to the lower molten viscosity. Optimum application temperature of T-558-N is in the
range of 180C~200C.
T-558-N shows excellent adhesion onto various types of plastics,
and steel, as well as onto many other surfaces, giving very tough bonding and sealing strength.
T-558-N may be applied either by hand or manually operated by hand-guns.
An automatic dispensing equipment with a nozzle or a wheel applicator may also be benefited.
KINGMIDE H-175SP is a high molecular weight polyamide resin especially designed for
hot melt-adhesive use. KINGMIDE H-175SP is easy to soluble in mixed organic solvent,
such as toluene and alcohol type solvent.
This resin has the characteristics of high softening point, and high molten viscosity
so that it is suitable for applications where high heat resistance and high
adhesive strength and good toughness.
KINGMIDE 328-A is a Polyaminoamide type epoxy curing agent.
Mixtured resin of KINGMIDE 328-A with an epoxy resin maintain a rather longer pot-life,
and provides its cured products with well balanced cured properties.
KINGMIDE 328-A is a therefore recommended to be employed
for such applications as general adhesives and structural adhesives
in construction works.
KINGMIDE 310 is a polyaminoamide curing agent for liquid epoxy resin to achieve fast
cure more than KINGMIDE 305 at ambient temperature.
It has a high molecular weight and provide the cured products with high orders of flexibility, adhesion,
good chemical and water resistance. The major applications of KIMGMIDE 310 are for general adhesives,
civil engineering and construction.
KINGMIDE 423-HPP is a reactive modified polyamide curing agent for epoxy resins.
KINGMIDE 423HPP is cut to 60 percent solids by weight in xylene/ isobutanol .
When cured with high molecule weight of epoxy resin.
It is provides cured films with such high orders desired at
actual application field as good flexibility, simultaneously with good water resistance and good
alkali resistance. Especially for heavy duty primer coatings application of anti corrosion
resistance.
KINGMIDE 305-70 curing agent is a standard reactive polyamide intended for use in curing
of epoxy resin. KINGMIDE 305-70 is cut to 70 percent solids by weight in xylene/ isobutanol.
Whem cured with ac high molecule weight of epoxy resin.
It is provides cured films with such high orders desired at actual application field as good flexibility,
simultaneously with good water resistance and good alkali resistance.
KINGMIDE 305-70 is thus desired for heavy duty primer coatings application of anti
corrosion resistance. Viscosity ( Gardner Holdt/25C degree ) - W~ Z.
KINGMIDE 300-65 is a polyamide type epoxy curing agent synthesized by polymerized
fatty acid and polyamines.
The resin component of KINGMIDE 300-65 is designed for high molecule weight and it is
therefore semi-solid in its form at an ambient temperature. However, for easy handling
at an actual application works, KINGMIDE 300-65 is dissolved
in the manufacturing process before being released to the users.
KINGMIDE 300-65, when cured with an epoxy resin, provides its cured films with such high
orders desired at actual application field as good flexibility, simultaneously with good water
resistance and good alkali resistance.
KINGMIDE 300-65 is thus desired for heavy duty primer coatings application of anti
corrosion resistance.
Viscosity (Gardner Holdt/25C degree )- Z ~ Z6.