Super Heat Duty and High Alumina Fire Bricks arethe products made fromdifferent fractions of refractory grog, fire clays and calcinedbauxiteof high purity.Thedifferent fractionsof theserawmaterials aremixedin counter current mixers and plugged for obtaining homogeneous mixture. The mixtureobtained hence,is then pressed in high capacity presses to give the desired shape and size.These pressed shapes are fired in high temperature tunnel kiln at
1300 C and above. These bricks are manufactured as per IS: 6 and IS: 8
Shape RECTANGULAR // CUSTOMISED
Brick/Block Color BROWN
For Use in Side Walls, Partition Walls, Roof, Floor
Brand GLM
Material CLAY AND ALUMINA / BAUXITE
Size 9 In. X 4 In. X 3 In.
High alumina brick for blast furnace;
Burned micro hole carbon-high alumina brick for blast furnace;
Normal high alumina brick for hot blast stove;
Low creep high alumina brick for hot blast stove;
High alumina brick for electric arc furnace roofs;
High alumina brick for steel ladle.
We offer premium quality acid resistant bricks, tiles and special shapes. We also offer customized Shapes and sizes as required by our customers.
We offer FIRECLAY and RED SHALE Type ACID RESISTANT BRICKS and TILES
sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 , IS 4860
Boiler Crushed Refractory Bed Material. The products we offer are developed by a team of diligent professionals in accordance with international quality norms. In order to ensure the safe transits of offered boiler crushed refractory, we provide these in pack of 40-50 kg plastic waterproof bags.
Moreover, we are capable of providing these products to the clients in bulk amount in accordance with their needs.
Special characteristics-:
Fully Screened Material Free From Fine Particles
Fully Resistant Against Clinker Formation
Perfect Product For Obtaining Fluidized Action
Accurate Particle Size Distribution
Exceptional Chemical Purity
High,I.D.T.(Initial Deformation Temperature)
Low Alkali Low Iron Contents
No Free Iron Particles-Passed Through Iron Separators
Perfectly Controlled Density
Production capacity: 1000 Tons per month
Delivery time: Ex-stock
Minimum order quantity: 15 Metric Ton
The bricks we offer are widely applauded for their dimensional stability, compressive strength and durability. Moreover,
Super Heat Duty and High Alumina Fire Bricks are the products made from different fractions of refractory grog, fire clays and calcined bauxite of high purity. The different fractions of these raw materials are mixed in counter current mixers and plugged for obtaining homogeneous mixture. The mixture obtained hence, is then pressed in high capacity presses to give the desired shape and size. These pressed shapes are fired in high temperature tunnel kiln at 1300�°C and above. These bricks are manufactured as per IS: 6 and IS: 8 specifications and high alumina in the range HEAT 5050 TO HEAT 88 in standard, arch and special shapes.
we provide these quality assured bricks to the clients at nominal rates.
We are manufacturers for CFI( Cold face insulation) & HFI (Hot face insulation) Bricks.The bricks are manufactures as pre clients requirements and sizes provided.
Insulation bricks are light weight bricks compared to other refractory Bricks.
Super Heat Duty and High Alumina REFRACTORY TILES arethe products made fromdifferent fractions of refractory grog, fire clays and calcinedbauxiteof high purity.Thedifferent fractionsof theserawmaterials aremixedin counter current mixers and plugged for obtaining homogeneous mixture. The mixtureobtained hence,is then pressed in high capacity presses to give the desired shape and size.These pressed shapes are fired in high temperature tunnel kiln at
1300 C and above. These bricks are manufactured as per IS: 6 and IS: 8 specificationsand highaluminain therange HEAT50 TOHEAT85 in standard, arch and specialshapes. weprovidethesequalityassuredbricksto theclientsat nominalrates.
Super Heat Duty and High Alumina KILN CAR BLOCKS arethe products made fromdifferent fractions of refractory grog, fire clays and calcinedbauxiteof high purity.Thedifferent fractionsof theserawmaterials aremixedin counter current mixers and plugged for obtaining homogeneous mixture. The mixtureobtained hence,is then pressed in high capacity presses to give the desired shape and size.These pressed shapes are fired in high temperature tunnel kiln at
1300C and above. These bricks are manufactured as per IS: 6 and IS: 8 specificationsand highaluminain therange HEAT50 TOHEAT85 in standard, arch and specialshapes. weprovidethesequalityassuredbricksto theclientsat nominalrates.
Features need for our brick
* Its high compressive strength and low water absorption make it perfect for applications such as groundwork, retaining walls and damp-proof courses
* The Red Class B Engineering brick is a smooth red perforated Wirecut brick
* Smooth texture
* Perforated
* Wire cut
Technical Information
* Size: 215 x 102.5- 65 mm
* Compressive strength: 75N/mm
PRODUCT DATA SHEET ACID RESISTANT BRICK
Material : FIRECLAY Type Acid Resistant Brick
Size (mm) : 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK)
Specification : ASTM C279, ASTM C410, IS 4860-1982
DESCRIPTION :
* We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required.
FEATURES OF ACID RESISTANT BRICK:
* Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature
AREA OF APPLICATION:
Chemical Analysis (Average)
Acid and Alkali Storage Tank Farms
Demineralization plants and Water treatment plants
Chimney inside lining, FGD linings
Towers and Columns
Process Vessels and Tanks
Sewerage Treatment Plants and Lines
Industrial Flooring and Bund Areas
Chimney and Flue Gas Linings
Hoppers and Chutes
SiO266.4
Al2 0324
TiO21.1
Fe2 O31.1
K2 O + Na2 O2.5
NOT RECOMMENDED:
HF acid or other fluoride solutions - Heavy thermal shock
Characteristic
Fireclay Type Acid Resistant Brick - Test Standard
Bulk Density, lbs/ft3 - 2.25 to 2.30 ASTM C-20
Water Absorption, % - 0.1 to 1.8 ASTM C-20
Apparent Porosity, % - 4.05 to 4.14 ASTM C-20
Acid Solubility (H2SO4), Loss in Mass,% - 6.1 to 6.8 ASTM C-279
Modulus of Rupture, Mpa - 14.6 ASTM C-67
Compressive Strength, PSI - 15500 to 17250 ASTM C-67
Abrasion Resistant , Volume in mm3 - 71 to 96 EN 102
Surface Hardness, MOHS Scale - 7
Thermal Conductivity, BTU-in/hr-ft-F - 6.94 to 7.12 ASTM C-236
Thermal Expansion Coefficient,in/in/Fx10-6 - 2.6 to 2.8 EN 103
PRODUCT DATA SHEET ACID RESISTANT BRICK
Material : RED SHALE Type Acid Resistant Brick
Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK)
Specification : ASTM C279, ASTM C410, IS 4860-1982
DESCRIPTION :
We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required.
FEATURES OF ACID RESISTANT BRICK:
Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature
AREA OF APPLICATION:
Chemical Analysis (Average)
Acid and Alkali Storage Tank Farms
Demineralization plants and Water treatment plants
Chimney inside lining, FGD linings
Towers and Columns
Process Vessels and Tanks
Sewerage Treatment Plants and Lines
Industrial Flooring and Bund Areas
Chimney and Flue Gas Linings
Hoppers and Chutes
SiO266.4
Al2 0324
TiO21.1
Fe2 O31.1
K2 O + Na2 O2.5
NOT RECOMMENDED:
HF acid or other fluoride solutions
Heavy thermal shock
Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick
Characteristic
RED SHALE ACID RESISTANT BRICK
Test Standard
Bulk Density, gm/cc - 2.3 to 2.35
ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968
Apparent Porosity, % -0.5 to 1.75 S 4860
Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279
Modulus of Rupture, PSI -2133 to 3555 ASTM C-67
Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968
Abrasion Resistant , Volume in mm3 -69 to 85 EN 102
Surface Hardness, MOHS Scale - 7
Magnesia Bricks Description
Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application.
Magnesia Bricks Features:
It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature.
Magnesia Bricks Application
Basic open-hearth furnace for steelmaking
Electric furnace bottom and wall
Permanent lining of oxygen converter
Non-ferrous metal metallurgy furnace
Hyperthermia tunnel kiln
Lining of rotary cement kiln
Heating furnace bottom and wall
Regenerative chamber of glass furnace
Magnesia Bricks Properties
High Refractoriness
Good alkaline slag erosion resistance
High apparent initial softening temperature
Good thermal conductivity
High thermal expansion
Magnesia Bricks Manufacturing Process
Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.
ALUMINA MORTAR (Test Certificate)
General Properties
A. Max service temperature - 1500 oC
B. Maximum grain size - 0 - 1.5 mm
C. Water required for mixing - 22 - 30%
D. Setting - Airsetting
E. Sintering Temp - 1550 oC
Chemical Properties
A. Al2O3 - 50.00%
B. SiO2 - 31.00%
c. Fe2O3 - 5.00%
D. LOI - 7.00%
Physical Properties
A. Dry Density - kg / m3
B. CCS - 17 kg / cm2 after drying at 110C / 24 hr
C. MOR - 20 kg / cm2 at 110 oC/ 24 hr
18 kg/cm2 at 800 C/ 3 hr
Thermal Properties -
A. Refractoriness ( Orton / C) - 31.5 orton cone/1699 oC
Packaging - 25 - 50 kg bags
Storage Life - 12 months
Delivery State - Dry