Silicones are synthetic polymer containing alternate silicone and oxygen atoms as its backbone. Silicones are made from silicon (a metal obtained from silica sand) and methyl chloride (an organic compound) in a process known as the direct process. The Silicone sealant in the uncured state normally looks like a thick paste or cream. After curing the paste turns into an impressive rubber.

Applications
Silicone sealant are used as a form-in-place gaskets for engine & transmission applications, sealing of exterior joints, aquarium joints bonding, sealing of bath tubs, construction and glazing application, electrical potting & encapsulation, mould making, etc.

Curing Mechanism
RTV silicone systems use humidity or moisture in the air during curing and cannot be accelerated using heat (excessive heat in the curing process can be detrimental). Small amounts of by-product are also produced. The cure process will only take place if the material is open to the atmosphere and curing will be adversely affected if access to humidity is removed prior to the completion of the cure process.

Provided product types
One component RTV silicone sealant
Two component RTV silicone sealant
Packing, storing, shelf life and transport
Available packing sizes vary from 25 g to 25 kg, packed in lacquered coated aluminium tubes, HDPE cartridges and epoxy coated MS drums. Store products at room temperature (20C to 35C). Shelf life can vary from 4 - 12 months. They are safe to transport by road, air and sea.

Silicone sealant equipment produced by JCT company,Well made,Reasonable structure,Easy to operate,Suitable for the production of a variety of silicone sealant.
We can provide custom-made for you .
.Production line specifications:
1)30-60 tons / month silicone rubber production line;
2)60-120 tons / month silicone rubber production line;
3)120-360 tons / month silicone rubber production line;
4)150-450 tons / month silicone rubber production line;
5)300-600 tons / month silicone rubber production line;

Wholesale high temperature silicone rubber thermal electrically conductive grease

CAS No.:7085-85-0
Other Names:Silicone Sealant
MF:Mixture
EINECS No.:230-391-5
Place of Origin:Guangdong, China (Mainland)
Classification: Double Components Adhesives
Main Raw Material:Silicone
Usage:heat sink
Brand Name:laimeisi
Model Number:lms
Type:silicone thermal grease, Silicone Grease
Color:as picture show
Material:silicone Rubber
Application:heatsink
Certificate:ROHS
Product name:Wholesale high temperature silicone thermal conductive grease
Keywords:thermal conductive grease
Appearance:White and Grey Paste
Quality:Top-quality
Shelf life:12 Months

Packaging & Delivery
Packaging Details:as customer requiremnet/
/pp bag and standard carton, or customized packing
Delivery Detail:Shipped in 7 days after payment

1. Grade: High temperature silicone thermal conductive grease
2. Standard: LMS
3. Certification: ISO9001, SGS, CTI, ROHS


Product NameWholesale high temperature silicone rubber thermal electrically conductive grease
MaterialSilicone Thermal Grease
ColorGrey and white
Thermal conductivity 1.5~6w/mk
working Temperature-40~220°C
Shelf life12 month(10~28°C)

Feature of High temperature silicone rubber thermal electrically conductive grease
1. Made from high quality silicone material,
2. Certificated by kinds of certifications,
3.Suitable for auto-dispensing and screen printing
4.High thermal conductivity, low thermal resistance.
5.Low bleed, low evaporation rate.
6. stable at high temperatures


Application of High temperature silicone rubber thermal electrically conductive grease
1.electronic components: IC, CPU, MOS
2.LED, M/B, P/S, Heat Sink,
3.LCD-TV, Notebook PC, PC, Telecom Device, Wireless Hub?¦..etc
4.DDR ll Module, DVD Applications, Hand-set applications?¦..etc
5.Between a CPU and a heat spreader.

Water Treatment
DEHA is used in Water Treatment Chemical Formulations for controlling corrosion in boiler very effectively due to its property of oxygen scavenge scores over conventional hydrazine hydrate since it is far less toxic and meets the standard for disposal of blow offs without any difficulty giving good protection against corrosion at the same time.
Polymerization
DEHA's powerful free radical scavenging ability coupled with its moderate volatility and relatively low order of acute toxicity makes it an ideal "po Polymer "/ vapour phase inhibitor for olefins or styrene monomer storage & recovery system. Because of its capability of inhibiting polymerlzatlot the gas phase, DEHA is finding use as an in-process inhibitor for the production of styrene, divinylbenzene, butadiene, isoprene and other monorr containing a reactive double bond.
â?¢ Photographic Chemicals
DEHA has reducing property, so it is used as an auxiliary chemical photographic developer for instant colour photos. Also, DEHA is effective in stabilization of image and in the prevention of discolouration.
Decolourisation
Phenol and Phenolic antioxidants can be decolourised with DEHA.

Inhibitors
DEHA also can be used as a colour stabiliser of monoalkyl phenol. Silicon Rubber
DEHA can be used as a raw material for the hardener of the Silicon Sealant and coating agent.

Storage
Can be stored and handled in equipment made of stainless steel of Type SS304 or SS316 or steel lined with glass, polypropylene or polyethylene
Storage in mild steel equipment or containers is not recommended.
DEHA drums should be stored in a cool and well ventillated area, away from sources of ignition. Forms two layers for concerntration from 33 to 87 wt %.
Packing
25 kg, 180 kg net wt. in HMHDPE carbouys & drums .
Health &Safety
DEHA is irritating to skin,eyes and the mucous membrane.
In case of contact,affected area to be washed with plenty of water for atleast 15 minutes.
In case of inhaltion,victim should be moved to fresh air and oxygen should be administered.
In case of ingestion,victim should be made to consume copious quantity of milk and water. Medical advice should be sought at once. Personal protective equipment should always be used while handling.

Two-component polysulfide sealant, as known as a two-component, non-sag, premium polysulfide sealant, which is also called polysulfide sealant for building made up of liquid polysulfide rubber, and add tackifying resin, vulcanizing agent, accelerant and fortifier into it. It contains two components and it can vulcanize and crosslink by itself at room temperature. The two components have clear color difference, which makes the mixing more convenient. It can keep good air tightness and water resistance in continuous vibration and temperature changes. In addition, it has a good bonding effect for metal, concrete and other materials.

Application
The polysulfide sealant is suitable for outdoor or indoor and can be used to seal both static and dynamic joints:

Used to caulk at concrete, building, and bridge.
Used in anti-leakage caulking of various types of expansion joints, such as waterworks, swimming pools, reservoirs, power plants, dams, sewage treatment works and water supply and drainage systems and other projects.
Used as the joints of precast concrete, and the seams of the glass and construction.
Used in the seaming of metal siding, and the bonding of aluminum window frame.

Using method

Add component B and pigment into component A;
Stir quickly up and down until it is well mixed;
Wipe the mixed sealant in the site where is waiting for construction with a small shovel;
Don´t soak and contact with water within 48 hours after construction.
Note

Component B should be fully added into component A, which will affect the curing time and plasticity;
The available time of mixed sealant is 2 hours. So the sealant should be used up as soon as possible after preparation to avoid the paste curing;
The surfaces waiting for construction must be clean, dry and frost-free, and must be free of oils, grease, paints, coatings, sealers, curing compound residues, and any other foreign matter that might prevent adhesion;
Notice to avoid water and rain within 48 hours after construction.

Descriptiion
CS-500 is a sealant mainly made by specialized rubber polymer,
compatible with surface of various materials.
Especially suitable for architectural expansion joint and crack
repairing applications.

Use
1.Used for sealing joints in applications such as curtainwall joints,
metal panel joining,bedding thresholds,secondary glazing seals.
2.Standing seam roofs, side walls, gutters and downspouts sealing.
3.Filling and caulking joints in heating and air conditioning ducts.
4.Joint sealing in sheet metal.

Feature
1.Excellent thixotropy,non-sagging during vertical application.
2.Good durability and flexibility.
3.Compatible with various kinds of paint.

Color
grey

Packaging
300ml cartridge

Product Description:
Chemical Name: 3-Glycidoxypropyltrimethoxysilane
CAS NO. : 2530-83-8
Against other brands: Einecs#:219-784-2
Silquest A-187*
Dow Corning:Z-6040/OFS-6040
ShinEtsu: KBM-403
Degussa: Dynasylan Glymo
Wacker: Geniosil GF 80.

Specifications:
Appearance : Colorless transparent liquid
Color (Pt-Co): 25
Specific Gravity20C, g/cm3 1.060 1.075
Refractive Index : 1.4275 1.4300
Purity% : at least 97.0

Applications:
1. As epoxy coupling agent, it is used in polysulfide-based and metal-filled epoxide resinous material.
2. Improve the adhesion between inorganic stuffing, substrate material and resin, accordingly improve electrical property of electronic material which is made of epoxy resin and wrappage.
3. It can be widely used in multi-fillers and substrates such as clay, talcum, tricalcium silicate, silica, quartz, aluminum, copper and iron. Including quartz-filled epoxy sealants, grail-filled epoxy resin and concrete patching material or coating, toner of modeling kits, and improving the dispersivity, fluidity of adhesive.
4. To avoid the need of independent primer in polysulfide and polyurethane sealant and sealing compounds.
5. Improve the adhesion of double-component epoxy sealing agent, It is used in polyurethane adhesive and sealant, epoxy resin adhesives, enhanced thermosetting resin, glass fiber adhesive, thermoplastic resin for inorganic filler or glass reinforcement.





25 kg, 200kg plastic or iron drum.

Product Description:
Chemical Name : gamma-aminopropyltriethoxysilane
CAS NO. : 919-30-2
Against other brands: Einecs No:213-048-4
Silquest A-1100*
Dow Corning: Z-6011
ShinEtsu: KBE-903
Degussa: Dynasylan AMEO
Wacker: Geniosil GF 93.

Specifications:
Appearance : Colorless transparent liquid
Colour (Pt-Co) : 25
Specific Gravity20C, g/cm: 3 0.940 0.950
Refractive Index : 1.4180 1.4220
Purity% : at least 97.0.

Applications:
Coatings, Adhesives and Sealants:
The aminosilane is an excellent adhesion promoter in acrylic coatings, adhesives and sealants. With polysulfide, urethane, RTV silicones, epoxy, nitrile, phenol formaldehyde resin, adhesives and sealants, the product improves pigment dispersion and maximizes adhesion to glass, aluminum and steel.

Fiber glass Reinforcement:
In fiberglass reinforced thermosetting plastics and thermoplastics, the aminosilane enhances the flexural, tensile and interlaminar shearing strengths before and after exposure to humidity. This product greatly improves wet electrical properties. Fiberglass reinforced thermoplastics, polyamides, polyesters and polycarbonates exhibit increased flexural and tensile strengths before and after wet exposure when this silane is used.

Glass Fiber and Mineral Wool Insulation:
As a phenolic resin binder additive, the aminosilane imparts moisture resistance and allows recovery after compression

Mineral Filler and Resin Systems:
The aminosilane maximizes the physical and electrical properties of mineral-filled phenolics, polyester resin, epoxies, polyamides, polycarbonate and a host of other thermoset and thermoplastic composites. Wettability and dispersibility of filler in the polymer matrix are also improved.

Foundry Application:
In shell molding, the aminosilane strengthens the bond between the phenolic binder and foundry sand.

Grinding Wheel Manufacture:
The aminosilane promotes an improved, water resistant bond between the abrasive grit and phenolic resin binder.

Wood plastic composite production:
The mechanical properties of composites made of wood meal, such as impact strength, bending strength and bending modulus, will be improved after these composites are processed with this product.






25 kg, 200kg plastic or iron drum.

Manufacturer leading quality OH Terminated Polydimethylsiloxane CAS: 70131-67-8
High molecular OH-terminated Polydimethylsiloxane

CAS No. :70131-67-8

MOLECULAR FORMULA :HO[-Si(CH3)2O-]nH

Other Names:
107hydroxy silicone oil, Hydroxy polydimethylsiloxane, Hydroxyl-terminated polydimethylsiloxane, OH-termianted silicone oil, OH-terminated silicone polymer, High molecular hydroxy silicone oil, Hydroxy end group polydimethylsiloxane, OH Polymer, Dihydroxyl polydimethylsiloxane, Hydroxyl dimethyl polysiloxane, Silanol-terminated polydimethylsiloxane, Polydimethylsiloxane silanol Terminated.

JP107 Polymer Hydroxyl silicone oil is the organosilicon material polymerized by siloxane monomer terminated with hydroxyl groups . Conventionally the hydroxyl silicone oil with viscosity above 1500 mpa.s is called 107silicone sealant/adhesive.

Apart from general functions of hydroxyl silicone oil, this product possesses the reactivity of hydroxyl group that can be made into some new material or crosslinked as elastomer(or film body). This product is colorless transparent liquid with excellent electrical insulation, high and low temperature resistance,high flash point, low freezing point,long-term adaption to temperature from -50°C to 250°C, low viscosity-temperature coefficient, high compression rate, low surface tension, good water repellent and moisture resistance, chemical inertness, physical inertness.


[MAIN PROPERTIES]

Excellent waterproof and dustproof performance;

Sealing for various installation of aluminum alloy glass doors and windows;

Sealing for organic glass, polycarbonate.

Excellent weather resistant performance and excellent ageing resistant performance;

Excellent adhesion to most of building materials and excellent compatibility with other neutral silicone sealants.


APPLICATION

Used as main raw material in RTV mold silicone rubber, defoamer and silicone glass cement.

1. Used as insulating, moisture resistant, anti-shock and heat resistant perfusion sealing material in radio, electronic equipment, semiconductor and other electronic components and assemblies.

2. Used as rubber roller material in automobile and machinery industry.

3. Used as rubber roller material in textile, plastic and printing industry.

4. Caulking sealing material in construction industry.

5. It has excellent mold release performance, particularly suitable for the manufacture of precision mold and impression materials.