Properties: The product is a white crystalline powder or a sandy-size granularity, and a pinkish crystalline powder or a sandy-size granularity as well. Sp.gr.2.953.01g/cm3, melting point about 1000centigrade, specific heat 1.056j/gcentigradeat 18100centigrade. Its slightly soluble in water, but insoluble in anhydrous hydrogen fluoride. The content of its crystal water will be decreased while the increasing of the molecular ratio, therefore its loss on ignition will be also decreased while the increasing of the molecular ratio. After the paste of synthetic cryolite with different molecular ratio dehydrates, the loss on ignition at 800centigrade will appear 10.34%, 6.22% and 2.56% when the molecular ratio reaches 1.74, 2.14 and 2.63 reactively.
Specifications:
Appearance white powder
F 52% min
Al 12% min
Na 33% max
SiO2 0.36% max
Fe2O3 0.08% max
CaO 0.5% max
P2O5 0.03% max
SO4 0.6% max
H2O 0.4% max
Loss on ignition 2 % max
Uses: Its mainly used as a flux in the aluminum smelting by fused-salt electrolysis; also an opalizer in the manufacture of enamel; an opacifier and auxiliary solvent of glass and enamel; an insecticide of crops; a flux in aluminum alloy casting; and in the production of ferrous alloy and effervescing steel; as well as a wear-resistant filler for resin and rubber-boned abrasive wheels.
Packing & Storage: In plastic coating woven bags with plastic film inside, 25kg,40kgs, 50kgs or 1000kgs net each, or as the requirement of clients.Stored: in a cool , ventilated, dry place.
Prperties: The prduct is a white needle crystal r pwder. SP. GR. 2.8823.13g/ cm3, sublimatin temp. 1272Celsiur scale.Its slightly sluble in water and greatly sluble in HF liquid. The chemical prperty fr the high density aluminum fluride is very steady, but that cntains certain crystal water will be decmpsed int Al23 at high temperature with HF being released.
Specificatin:
grade chemical cmpsitin % Physical character
F Al N2 Fe2342- P25 LI Bulk dity g/cm3
AF-0 61.0 31.5 0.30 0.10 0.06 0.10 0.03 0.5 1.5
AF-1 60.0 31.0 0.40 0.30 0.10 0.6 0.04 1.0 1.3
AF-2 58.0 29.0 2.8 0.30 0.12 1.0 0.04 5.5 0.7
AF-3 58.0 29.0 2.8 0.35 0.12 1.0 0.04 5.5 0.7
Uses: Its mainly used as an adjusting agent fr electrlyte in aluminum smelting by fused salt electrlysis, als in ceramic glaze, catalyst and flux f nnferrus metal metallurgy etc.
Brief Intrductin f the Prductin Technics
In the Hydrgen Fluride Reacting Furnace which is heated utside, Vitril reacts with Flurite t create the Hydrgen Fluride Gas and Anhydrus Fluride Plaster by heating in the prcess f prducing Aluminum Fluride, then the Hydrgen Fluride Gas react with dry Aluminium Hydrxide in Fluidized Bed t create t Aluminum Fluride and water.
Packaging
packed in wven PP bags with plastic film inside. Each bag has net weight f 25kgs, 50kgs, 500kgs and 1000kgs.
Properties: White monoclinic crystalline powder with sulfur dioxide odor; relative density: 1.49; very easily soluble in water; can be decomposed when heated; slightly soluble in ethanol; aqueous solution is acidic; has strong reducing property; can be oxidized in the air or loose sulfur dioxide.
Use: It is used in the bleaching of cotton textiles; as reducing agent in dyes, paper-making, leather, chemical synthesis; in the manufacture of pharmaceutical intermediates, developer, food bleacher, antiseptic and anti-oxidants.
Packing: In PP woven bag lined with PE bag; paper-plastic composite bag, and kraft paper bag etc.
Net wt.: 25/50/1000 kgs/bag or upon clients' request.
Since 2010 we are engaged in trading & exports of ceramic products, very high Quality of Zirconium Silicates & Zirconium Flours for ceramics.
We mostly supply Zirconium 2, Zirconium 5 and Zirconium Flour 325 mesh to ceramic industries.
Application Of Zirconium Silicates :
Opacifier for pottery and porcelain glazes ,wall tiles, roofing tiles, sanitary ware etc
Frits, Glazes & Enamels.
Admixture for ceramic body. (Improvement of property and Opacification of color)
Calcined Bauxite is obtained by calcining (heating) superior grade Bauxite at high temperature (from 850 oC to 1600 oC). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, Calcined Bauxite has an alumina content of 82 % to 86 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 oC to 1600 oC depending upon the customer’s application.
We export Calcined Bauxite for various applications such as refractory bricks, abrasives, steel polishing, etc. We provide consistency in quality and availability of Calcined Bauxite at extremely competitive prices.
Applications of Calcined Bauxite:
Refractory Grade Calcined Bauxite (CB - I and CB - II Grade) : To make refractory grade, Bauxite is thermally treated at 1600 oC to produce Calcined Bauxite where the Alumina content is mostly above 82%.
Brown Fused Alumina, Proppants and Road Surfacing : To make the above grades, Bauxite is thermally treated at 1000 oC - 1200 oC to produce Calcined Bauxite where the Alumina content is anywhere between 80-88% depending on the requirement.
At Johneliz Global Investment Limited, we provide premium-quality Corundum, one of the hardest natural minerals, second only to diamond. Renowned for its exceptional hardness and durability, corundum is widely used in industrial applications such as abrasives, cutting tools, grinding wheels, and sandpapers. In its pure, transparent form, corundum also forms the basis of precious gemstonesâ??ruby and sapphireâ??valued in the jewelry industry. Our corundum is carefully sourced and processed to ensure high purity and consistent performance, meeting the strict specifications required for both industrial and ornamental uses. Johneliz Global Investment Limited is committed to delivering top-grade mineral products, supporting a variety of sectors with reliable quality, technical support, and timely global distribution.
Melting point 151-154 C(lit.)
Boiling point 265 C100 mm Hg(lit.)
Density 1,36 g/cm3
vapor density 5 (vs air)
vapor pressure 1 mm Hg ( 159.5 C)
refractive index 1.4880
FEMA 2011 | ADIPIC ACID
Flash point 385 F
storage temp. Store below +30C.
solubility methanol: 0.1 g/mL, clear, colorless
pka 4.43(at 25)
form Solid
color White
Odor wh. monoclinic prisms, pract. odorless
PH 3.74(1 mM solution);3.22(10 mM solution);2.71(100 mM solution);
Water Solubility 1.44 g/100 mL (15 C)
Merck 14,162
JECFA Number 623
BRN 1209788
Exposure limits ACGIH: TWA 5 mg/m3
Stability Stable. Substances to be avoided include ammonia, strong oxidizing agents.
InChIKey WNLRTRBMVRJNCN-UHFFFAOYSA-N
LogP 0.09 at 25â??
FDA 21 CFR 184.1009; 582.1009; 175.300; 175.320; 177.1680
Substances Added to Food (formerly EAFUS) ADIPIC ACID
SCOGS (Select Committee on GRAS Substances) Adipic acid
CAS DataBase Reference 124-04-9(CAS DataBase Reference)
EWG's Food Scores 1
FDA UNII 76A0JE0FKJ
NIST Chemistry Reference Hexanedioic acid(124-04-9)
EPA Substance Registry System Adipic acid (124-04-9)
Magnesium oxide, often referred to as magnesia, is a white, odorless, and alkaline solid with the chemical formula MgO. It is recognized for its diverse applications across industries. In healthcare, it is used as an antacid to relieve heartburn and indigestion, as well as a magnesium supplement. In the construction sector, magnesium oxide is utilized as a refractory material in kiln linings and as a fireproofing agent in building materials. It also plays a role in metallurgy as a refractory lining material for furnaces. Additionally, magnesium oxide finds application in the production of electrical insulators, as a catalyst in chemical processes, and as a stabilizer in some food products. Its ability to withstand high temperatures, neutralize acidity, and serve various functions highlights its importance in different industrial and consumer applications.