Fire clay & High Alumina bricks are special type of brick which are form of Refractory ceramic material. It is used for inner surface lining of Boiler, furnace, kiln, fireplaces & fireboxes.
Quality of Bricks:
We offer various quality bricks are IS-6, IS-8, PI - 30% to 90% Alumina offering high temperature resistance of 1100 C to 1700 C.
Aluminum content: 25-42%
Compressive strength at room temperature: 30-45MPa
Standard brick size: 230*115*65mm
Cost-effective: The phosphoric acid impregnated products of blast furnace clay bricks with good thermal stability and qualified quality after drying treatment and secondary low temperature firing can be used for masonry of the upper part of the blast furnace furnace lining.
Good morning,
I am looking for supplying handmade clay bricks in minimum quantity 20000 to maximum 2000000. The price will be cheap and negotioable. Starting factory price £200/thousend excluding shiping and carring cost.
So please contact me for further details .
Premium Red Clay Bricks
Manufactured by Kishore Brick Works, India
The bricks are made from high-quality, top-tier natural clay and processed using fresh, non-saline water. They are hand-moulded with precision and machine-refined for uniform shape. The firing process uses high-grade coal in advanced kilns, ensuring exceptional strength and durability.
Available Sizes: 228 mm * 114 mm * 76 mm (9"* 4.5" * 3")
These bricks are ideal for load-bearing structures such as strong walls and pillars, real estate developments including residential and commercial buildings, and infrastructure projects like roads and bridges. They are also suitable for traders and importers of quality bricks.
Key Advantages:
Superior strength, long-lasting durability, eco-friendly production, and export quality.
Fireclay bricks are mainly made , being high pressure pressed and sintered in high temperature. Main minerals compositions are mullite phases. These products are widely used in all parts of furnace lining for middle and small capacity blast furnaces because of their excellent physical and chemical properties in high temperature. It also can be used in lining for other kinds of furnace.
1. Low bulk density, low thermal conductivity, good thermal insulation performance.
2. Refractory category allow direct contact of fire, suitable ofr various atmosphere
3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely
4. Can be used in various kilns because of its cheapness and general tray package.
Applications
1. Furnaces of metallurgy industry, heat treatment furnace
2. Furnaces of chemical industry and construction industry.
3. Furnace of incineration of garbage, recirculating fluidized bed furnace
Standard sizing: 230 x 114 x 65 mm others up to the client.
packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages.
Fire clay bricks are the most widely used refractories made from clay minerals. It can be easily located out in the nature and contains suitable content ratio of silica, cyanite and alumina. Some people call them fireplace bricks as they are usedor building cooking chamber in wood fired ovens, for creating fireplaces, all sorts of fire boxes and wood heaters lining, linings in a small or the hugest industrial furnaces, you name it. Fire clay bricks have low porosity and are durable for various re-heating process.
REFRACTORY BRICK
Refractory bricks refers to the brick whose Al2O3 contains from 30% to 80%, the contains of Al2O3 from 30% to 42% is call clay bricks, the contains of Al2O3 from 45% to 80% is call high alumina bricks.
Typical Parameters
Brief description
Clay brick is refers to the Al2O3 content is 30% ~ 40% aluminum silicate. Clay brick is made of soft clay and 50% and 50% of hard clay grog, ingredients required by certain granularity, after forming, drying, burning under the high temperature of 1300 ~ 1400 .Clay brick belongs to the weak acid refractory products, can resist acid slag and the erosion of acid gases, the alkali resistance ability is a bit poor. Clay brick has good thermal shrinkage.
High Alumina Brick selected calcined Bauxite and high quality combined clay as main raw materials. After shaped with brick machine above 600tons and fired at 1450-1470 °C , we can get this product. With high Al2O3 content, the product have good high temperature performance, so it is widely used in all kinds of industrial furnace and high temperature parts to prolong the life of furnace.
Products advantage
Clay Brick
1.Good acid stability
2.Good thermal performance
3.good thermal shrinkage
4.Good resistance to abrasion and corrosion
High Alumina Brick
1. High refractoriness, High-temperature endurable.
2. Good corrosion resistance.
3. Good spalling resistance and wear resistance.
4. Good thermal shock resistance.
5. High mechanical strength.
6. High-temperature creep rate is low.
7. Good volume stability at high temperature.
Typical Application
Clay brick is suitable for secondary parts of coke oven, such as regenerator seal wall, small flue lining brick and regenerator checker brick lining brick, roof, door and rising pipe lining brick, etc.It is one of refractory brick used in blast furnaces, hot blast stove, heating furnace, power boiler, lime kiln, rotary kiln, ceramics.
High alumina brick is mainly used for masonry in blast furnaces, hot air stoves, electric furnace roof, blast furnace and reverberatory furnace, rotary kiln lining. In addition, high alumina brick also widely used for open hearth regenerative checker brick, pouring system with plug head, gate brick, etc.
Average brick size: 220 x 100 x 60 mm
Bricks per pallet: 540 pieces
Pallets per container: 22
Bricks per container: 11.880 pieces
Total weight: Around 24.5 tonnes