Product Description:
Please provide a quotation to the following requirement from importer -
Product Name: Low Pressure Polyethylene Particles
Specification:
White Particles With Odorless, Odorless, And Non-toxic Properties. Melting Point 131 °C
Density 0.910-0.925g/cm3. Softening Point 120-125 °c. Embrittlement Temperature -70 °C.
The Maximum Operating Temperature Is 100 °C
It Has Excellent Heat Resistance, Cold Resistance, Abrasion Resistance, Dielectric Property And Chemical Stability. Almost Insoluble In Any Organic Solvent At Room Temperature. Capable Of Withstanding Corrosion From Various Acid, Alkali, And Salt Solutions. Low Water Absorption And Water Vapor Permeability. Tensile Yield Strength ( Mpa) More Than 23.0 Embrittlement Temperature ( Low-temperature Impact, °c) Less Than -70volume Resistivity (o Cm) 1 × Tendielectric Strength (kv/mm) More Than 35 Dielectric Constant 2.35 Dielectric Loss Angle Tangent Less Than 5 × Ten
This buylead is archived. Your inquiry will be sent directly to the buyer's email inbox, and they may respond at their discretion. However, you will not receive their contact details.
Buyer is interested to receive quotations for the following RFQ -
Product Name: Plastic Raw Materials
Specifications :
Type: Linear Low Density Polyethylene
LLDPE Melt 50 Equivalent to Sabic grade M500026 Used In Master Batch Production, Has To Be Produced By Reliance
Quantity Required : 1500 Ton/Tons
Please provide a quotation to the following requirement from importer -
Product Name: Low Density Polyethylene (LDPE)
Specifications :
DPE MP3425 Complies With The Requirements As Below Indicated When The Product Is Processed Using The Correct Practice And Testing Procedures
Properties
Unit
Test Method
Typical Value
Density ( Compound ) At 23ºc
G/cm3
ASTM D 792
0.934
Melt Flow rate 2,16 kg al 190ºC
g/10min
ASTM D 1238
0.25
Melt Flow rate 5kg at 190ºC
g/10min
ASTM D 1238
1.0
Carbon Black Content
%
ASTM D 1603
Greater Than 2
Vicat Softening Point
ºC
ASTM D 1525
98
Melting point
ºC
ASTM D 2117
124
Brittleness Temperature
ºC
ASTM D 746
Less Than -70
Tensile strain at break
%
ASTM D 638
22
Tensile elongation
%
ASTM D 638
Greater Than 600
Hardness
Shore D
ASTM D 2240
50
E.S.C.R. 10% igepal F50
Hr
ASTM D 1693-A
Greater Than 5000
Oxidation Induction Time 210 ºC
Min
ISO 11357
Greater Than 20