Silicone Chocolate Heart Mold

Product Description Food grade liquid silicone is used to .candy, cake and cholocate and soap mold and making artificial stone,cement and gypsum. Food grade quality silicone with nontoxic,Excellent fluidity, high tear and tensile strength, High duplication times repeated use, easy to demould,High temperature resistance and cure can be accelerated by heat Model 6210 6215 6220 6225 6230 Mixing ratio (A:B) 1:1 1:1 1:1 1:1 1:1 Hardness (Shore A)â?¥ 10 15 20 25 30 Tear-strength (kgf/c m�²)â?¥ 16 18 20 21 22 Viscosity (A/B mixed 25�°C mpa.S) 8000�±2000 8000�±2000 10000�±2000 10000�±2000 10000�±2000 Shrinkagerate (%)â?¤ 0.1 0.1 0.2 0.1 0.1 Elongation(%) 500 480 450 450 400 How to use: 1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent. 2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120�ºC for 30 minutes. 3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype. Package: 10KG, 20KG, 200KG or according to customer requirements.

Tin-based silicones, also called condensation-cure silicones, are two-component materials which cure at room temperature(RTV)to flexible, high tear-strength rubbers. Tin cured silicones can be poured onto models or they can be made brushable by adding a thixotropic additive. They are ideal for molds where easy release or high temperature resistance is required. Tin cured silicones can be used for casting polyurethane, epoxy and polyester resins, waxes, all gypsum products and low-temperature metals. Our tin-cured silicone systems are the most economical. They are best used for casting resins and low melt metals.

1.Product Description YJS-720 two components platinum cured silicone with 1:1 mixing ratio by weight. It is soft food grade silicone,  with 20 Shore A hardness, which is suitable used for moulding chocolate & icing sugar, candy, cakes, fondant.   2.Features: A. Amazing fluidity and easy to operate A. Platinum-based, food-grade silicone (environmental friendly, odorless and non-toxic) B. Delicate design available C. Mixing ration: 1:1, easy to mix D. Easy de-molding E. Excellent tension and tear strength F. High performance in duplication G. Shrinkage is almost zero (below 0.1) H. Excellent resistance to weather, temperature, aging, acid and aging-proofing. I. High resistance to high temperature and aging(resist -60 to 250) J. Food safe 3.Technical Data Typical general characteristics Inspection Method Value Product data (Catalyzed A+B) YJS-720 Hardness Shore A 20±2 Mix Ratio A:B 1:1/10:1 Color / translucent Pot life 25 °C (77F) 30-40mins Curing time 25 °C (77F) 3-4 hours Mixed viscosity mPa.s 5000±1000 Tear-strength kg/cm 20±2 Tensile-strength M.pa 4.0±1.0 Elongation % 500±50 Shrinkage % â?¤0.1% 4.Appearance: Part A: a non-toxic and odorless liquid with translucent color and platinum inside Part B: a non-toxic and odorless liquid with translucent color. ATT: We can do any curing time as your requirements.   Notice: What is the hardness should I choose Normally 5~55 Shore A will be the best, but it also should according to your size and pattern design. 5.SHELF LIFE: When stored at or below 32°C (89.6°F) in the original unopened containers, G-8 series Silicone have a usable life of 12 months. 6.Package 1kg/drum; 20kg/drum;25kg/drum;200kg/drum.

Item: OTT-S825 Mixing ratio:100:3 Color: White Hardness: 25;¨¤2 Viscosity (mPa.s):15000;¨¤3000 Working Time (25):20-40mins Curing Time (25):3-5h Tear-Strength (kN/m):;Y25 Tensile- Strength (Mpa):;Y4 Elogation (%):;Y500 Shrinkage(%):;¨¹0.2 1kg/tin 5kg/tin ;20kg/drum; 25kg/drum; ;200kg/drum

Factory price rtv2 silicone rubber for crafts molding Crafts Molding Silicone 1.Description 2. Technical Datasheet Typical general characteristics Inspection MethodValue Product data (Catalyzed A+B)C-820C-825 HardnessShore A20±225±2 Mix RatioA:B100:3100:3 Color/WhiteWhite Pot life25 °C (77F)30-40mins30-40mins Curing time25 °C (77F)3-4 hours3-4 hours Mixed viscositymPa.s16000±100020000±1000 Tear-strengthkg/cm20±222±2 Tensile-strengthM.pa3.6±0.54.0±0.5 Elongation%400±50450±50 Shrinkage%?¤0.3?¤0.3 Note: This is a 100A:3B mix ratio product that must be measured by weight. The choosing of suitable hardness should be according to the size and pattern design of the products. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise. 3. FEATURES Low viscosity,great flexibility,Extra low shrinkage,Chemical resistance,release properties, Easy to work with,High tear strength,Heat Resistance,various color is available,High reproduction rate 4.SHELF LIFE: When stored at or below 32°C (89.6°F) in the original unopened containers, C-8 series Silicone Base and its Curing Agents have a usable life of I0 months. 5.Package Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum. Curing Agent: 30g/bottle; 1kg/bottle

China supplier Rtv mould making Silicone rubber for Taxidermy Molding Taxidermy Molding Silicone 1.Description 2. Technical Datasheet Typical general characteristics Inspection MethodValue Product data (Catalyzed A+B)C-810C-825C-830 HardnessShore A10±225±230±2 Mix RatioA:B100:3100:3100:3 Color/WhiteWhiteWhite Pot life25 °C (77F)30-40mins30-40mins30-40mins Curing time25 °C (77F)3-4 hours3-4 hours3-4 hours Mixed viscositymPa.s6000±100020000±100023000±1000 Tear-strengthkg/cm12±222±223±2 Tensile-strengthM.pa2.0±0.54.0±0.55.0±0.5 Elongation%320±50450±50460±50 Shrinkage%?¤0.3?¤0.3?¤0.3 Note: This is a 100A:3B mix ratio product that must be measured by weight. The choosing of suitable hardness should be according to the size and pattern design of the products. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise. 3. FEATURES 1.Low viscosit 2.great flexibility 3.Extra low shrinkage 4.Chemical resistance 5.release properties 6.Easy to work with 4.High tear strength 5.Heat Resistance 6.various color is available 7.High reproduction rate 4.SHELF LIFE: When stored at or below 32°C (89.6°F) in the original unopened containers, C-8 series Silicone Base and its Curing Agents have a usable life of I0 months. 5.Package Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum. Curing Agent: 30g/bottle; 1kg/bottle