Descriptions:
Insulation brick is made from high purity refractory clays and other raw materials, with light
Weight and mini-porosity well distributed. It has advantages of low thermal conductivity, low
Heat storage, high spalling resistance, high hot compressive strength, how iron oxide and
Alkali flux content, accurate dimensions.
Applications:
It is widely used for insulating layer and lining of industrial kilns & furnaces.
Insulation Bricks are used for hot face & back up insulation lining of Boiler, Reheating furnace, Blast furnace, reactor chamber, high temperature furnace etc. Insulation Bricks are providing energy efficiency by minimising heat loss. They have feature of low density, high purity, low thermal conductivity, excellent thermal shock resistance. Types of Insulation Bricks: Cold Face Insulation Bricks Hot Face Insulation Bricks HFK Insulation Bricks Porosint Insulation Bricks Sizes: Standard 9 * 4.5 * 3 Inch
Acid Resistance bricks & Tile are special form of masonry bricks which are chemically resistant and thermally durable. These are used for masonry construction and flooring which is prone to chemical attack. These products are classified as per the different standard. Class - I Class - II Sizes of Bricks: 230 x 115 x 75 mm, 230 x 115 x 65 mm, 230 x 115 x 38 mm, 230 x 115 x 25 mm Sizes of Tile: 230 x 115 x 20 mm / 15 mm / 12 mm 200 x 100 x 20 mm / 15 mm/ 12 mm 300 x 300 x 15 mm / 12mm
Hanger & shoulder Fire bricks are special type of brick which are form of Refractory ceramic material. It is used for Roof lining of Boiler, furnace, kiln, fireplaces & fireboxes. Hanger & Shoulder Brick are used for Reheating furnace roof. There are three qualities of Hanger & shoulder brick as per their specification 40% Alumina Hanger & Shoulder Brick 50% Alumina Brick Hanger & Shoulder Brick 70% Alumina brick Hanger & Shoulder Brick
Cupola Fire Bricks are special type of brick which are form of Refractory ceramic material. It is used for inner surface lining of Boiler, furnace, kiln, fireplaces & fireboxes. Quality: We offer various quality bricks are IS-6, IS-8, PI - 30% to 70% Alumina offering high temperature resistance of 1100 C to 1700 C Sizes of Cupola Bricks: Length 9 Inch & 11 Inch Dia (Inch) 9D, 12D, 15D, 18D, 21D, 24D, 27D up to 56D
Supplier: Refractory bricks, high alumina bricks, acid proof bricks, tiles and castables, all mortars and fire clay, low cement castables, insulating castables, conventional dense refractory bricks, insulation bricks, cold face, hot face insulation bricks, hot face insulation bricks, acid resistant bricks/components, membranes, acid resistant cement, construction chemicals, class 1 ar tiles and bricks 38mm and 75mm, 4457 vitrified ar tiles with 0% water absorption, 20mm & 25m, primer, mastics, pot. silicate cement, coerce cement, furnace based cement, crushed refractory boiler bed material, acid resistant tiles, acid resistant brick fireclay type, acid resistant brick red shale type, bitumen primer, epoxy resin & hardner, furan powder and syrup solution,
Our company located in yangquan city, shanxi province, china, and yanquan city is one of the Largest refractory material base in china. We are in position to supply various kinds of Refractory bricks, such as high alumina and fireclay bricks, insulating bricks etc With the catalogue as follows: 1. Fireclay brick 2. High alumina brick 3. Insulating brick 4. Unsintered phosphate brick 5. Al-c sliding plate 6. Nozzle 7. Hollowwares 8. Refractory mortar 9. Refractory castables 10.Other refractory material.
Fire clay brick sk-32 ItemStandard Ai2o3(%)30 Fe2o3 (%)3.5 Refractoriness (sk)32 Refractoriness under load, 0.2mpa, ta, (°c)1300 Porosity (%)22-26 Bulk density (g/cm³)2.05 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6 Sk-34 ItemStandard Ai2o3(%)45 Fe2o3 (%)2.0 Refractoriness (sk)34 Refractoriness under load, 0.2mpa, ta, ((°c)1350 Porosity (%19-23 Bulk density (g/cm³)2.10-2.15 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6.
Sk-36 ItemStandard Ai2o3(%)55 Fe2o3 (%)2.0 Refractoriness (sk)36 Refractoriness under load, 0.2mpa, ta, ((°c)1450 Porosity (%20-24 Bulk density (g/cm³)2.2-2.30 Cold crushing strength (mpa)45 Thermal expansion at 1000°c (%)0.3 Sk-38 ItemStandard Ai2o3(%)75 Fe2o3 (%)2.0 Refractoriness (sk)38 Refractoriness under load, 0.2mpa, ta, ((°c)1520 Porosity (%20-22 Bulk density (g/cm)2.4-2.5 Cold crushing strength (mpa)55 Thermal expansion at 1000°c (%)0.2.
Y-fb gfb40 gfb42 gfb45 Al2o3(%)min. 40 40 42 45 Fe2o3(%)max. 2.5 Refractoriness()min. 1710 1730 1750 1750 Refractoriness under load 0.2mpa()min. 1300 1350 1400 1400 Apparent porosity(%)max. 22 20 20 20 Cold crushing strength (mpa)min. 30 30 35 40 Linear change after reheating(%)max. At 1350 2h +0.1 -0.4 At1400x3h +0.1 +0.1 +0.2 - 0.5 -0.4 -0.2.