Barrel & Screw For Injection Machine

Nitriding Commonly used for acid free plastics with GF less than 10%, such as PP PS AS ABS TPU TPE 38 CrMoAlA high quality alloy structural steel, quenching and tempering hardness HB260-280,nitriding hardness HV950±50 degrees, nitride layer depth 0.4-0.6mm, brittleness â?¤2

20 MM TO 150 MM Screw Barrel For Injection Moulding Machine

Specification: Screw diameter: d20mm-d220mm Mould clamping force: 250t-3200t Shot weight: 30g-30000g Technical information Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: ¡ã 950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm. Slushing oil coated& film wrapped in wooden case

Specification: Screw diameter: d20mm- d220mm Mould clamping force: 250t-3200t Shot weight: 30g-30000g Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: 950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm. Slushing oil coated& film wrapped in wooden case

Specifications Details: Technical Index: Depth of Nitrated Layer:0.5~0.8mm Hardness of nitration: 950~1100Hv Fragility of nitration: Less than grade 1 Surface Hardness of Nitrated Cr coating layer: 950Hv Hardness of Bimetallic Layer: HRC55~72 Thickness of Cr-coating Layer: 0.03~0.08mm Depth of Bimetallic Layer:>2mm Material :quality alloy steels 1.38CRMOALA 2.SKD61 3.stainless steel 4. Bimetallic Supply Capacity: Production Capacity: 1500 sets/month Packing: Fumigation wooden case Delivery Date: 30~40 days Screw Barrel Information: Super-hard plastic injection machine screw and barrel Choose a different screw screw head, barrel can choose the appropriate nozzle. Injection volume (g) Screw Diameter X Length (mm) barrel diameter X length (mm) 30-90 30x900 85x860 60-125 35x910 85x860 100-125 38x935 95x900 125-160 40x980 95x910 125-300 42x1030 105x880 250-400 45x1210 115x1165 300-500 50x1300 125x1260 450-600 55x1335 130x1320 500-700 56x1350 130x1350 500-700 60x1380 140x1350 650-800 65x1415 150x1420 700-1000 70x1790 160x1685 800-1250 75x1825 170x1725 1000-1500 80x2000 180x1805 1250-2000 85x2300 190x1900 2000-3000 90x2700 210x2000 2500-5000 100x2600 230x2405 3000-6000 110x2600 256x2590 4000-10000 120x2800 256x2800 6000-8000 130x3010 256x2970 8000-10000 145x3010 256x2970 10000-15000 160x3500 270x3200 13000-25000 170x3415 317x3380

Bimetallic screws Rigidity: HRC56~62 Applicable temperature: below 350 Applicable plastic materials: PA, PPT, PA with fiberglas, ABS, PC Applicable plastic products recommended: PA, ABC, PC Predominance: screw ridge surface wearable, perfect in adding less than 30% fiberglass and regenerate additive In wooden case

Parallel twin screw In wooden case

Specification: Screw diameter: d15- d 300 L/d ratio: 15-46 Product classification: Aiming at different plastic products the screw can be chosen from: general type, pin type, barrier type, separation type, and gas-exhausting type, etc. Base materials: (1)38crmoala(jis sacm645) (2)42crmo(aisi 4140) (3)4cr5mosi v1 (jis skd-61) (4)9cr18mov (5)hpt Bimetallic alloy materials: 1)fe-based alloy 2)ni-based alloy/deloro alloy 3)co-based alloy 4)nico-based alloy 5)tungsten carbide/wolfram carbide Technics: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Bimetallic alloy centrifugal casting Technical parameter: Nitrided layer depth: 0.5-0.8mm Nitrided hardness: 900-1000hv Nitrided brittleness: less than grade 1 Surface roughness: ra0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness after nitriding: >950hv Chrome-plating layer depth: 0.025-0.085mm Bimetallic layer depth: 3mm Slushing oil coated& film wrapped in wooden case

Over 29 years experience in screw and barrel , more info pls find kaylee(at)tizatech.com Specification: Diameter: Ã?15-Ã?500 L/D ratio:15-55 Base Materials: 1)38CrMoAlA(SACM 645) 2)42CrMo(AISI 4140) 3)Cr12MoV(SKD11) 4)4Cr5MoSiV1(SKD61) 5)9Cr18MoV 6)40Cr Bimetallic Alloy Materials: 1)Fe-based alloy 2)Ni-based alloy 3)Co-based alloy 4)Tungsten carbide Processing Technology: Heat treatment High-frequency quenching Nitriding treatment Hard-chrome electroplating Bimetallic alloy welding Technical Parameter: Nitrided layer depth:0.50-0.80mm Nitrided hardness: 900-1100HV Nitrided brittleness: Less than 2 level Surface roughness: Ra 0.4 Linearity of screw: 0.015mm Hard-chrome plating hardness: â?¥950HV Chrome-plating layer depth: 0.025~0.10mm Bimetallic layer depth: 2 mm Bimetallic hardness: HRC50-65 Material to be extruded: PP, PE, PVC, ABS, AS, PS etc. We can manufacture all types of screws and barrels according to clientsâ?? requirement