Ldpe/lldpe Rpg

lldpe/ldpe floor sweeps from film manufacturing only
mostly natural color contains small amounts of: purge, leaves, wood, cardboard, color concentrate
needs to go through wash line , 1load is available, loading weight : 35,000 pounds/cont
USA orgin, subject to unsold

LLDPE/LDPE 99/1 Transparent Color
MATERIAL: LLDPE/LDPE 99/1 Transparent Color
CATEGORY: LLDPE/LDPE
TYPE: 99/1
GRADE: Transparent color
SPECIFICATION: LLDPE/LDPE 99/1 from Korea
ORIGIN: Korea
LOADING WEIGHT: 25 Tons
CNF (USD/Ton): 700-900 Hai Phong, Vietnam

2Lians Recycling Pte Ltd can supply below scrap product:

LLDPE/LDPE Film Natural Color For Recycling
MATERIAL: LLDPE/LDPE film natural color
CATEGORY: LLDPE/LDPE
TYPE: Film
GRADE: Natural color
SPECIFICATION: LLDPE 80% LDPE 20% bales 50MT
Origin: Korea
LOADING WEIGHT: 21 Tons
FOB (USD/Ton): 680-780

LLDPE + LDPE Film Sorted Transparent 70/30 Plastic Scrap For Sales
MATERIAL : LLDPE + LDPE film sorted transparent 70/30
CATEGORY : LLDPE + LDPE
TYPE : Film
GRADE : Sorted transparent 70/30
SPECIFICATION : 70% LLDPE, 30% normal LDPE, no contamination
ORIGIN : Germany
LOADING WEIGHT : 20 Tons
FAS (USD/Ton): 650-900

HDPE:

HDPE cable material

Property Unit
Typical Value
Mass density g/cm 3 0.941-0.959
Melt flow Rate(190 centidegree /2.16kg) g/10min 1.0
Tensile yield strength MPa 19.0
Flexural modulus Mpa 965
Elongation@ break % 400
Impact Embrittlement temperature centidegree MAX -118
Dielectric Constant 100KHZ 2.32
1MHZ 2.31
Loss Tangent 100KHZ MAX 0.0001
1MHZ MAX 0.0001
Volume resistivity OHM-CM MIN 1x10 15
Application
Mainly used for the production of high toughness of the telephone,cable insulation material

LDPE:

Physical Properties Test Method Nominal Value Unit
Density ISO 1183 0.921 g/cm3
Melt Mass-Flow Rate (MFR) ISO 1133 1.9 g/10min
Hardness
Shore Hardness (shore D) ISO 868 45
Mechanical Properties
Tensile Modulus ISO 527-2 175 MPa
Tensile Strength Yield, ISO 527-2 9.0 MPa
Break, 13.0 MPa
Tensile Strain(Break) ISO 527-2 850 %
Modulus of Elasticity Internal Method 250 MPa
Thermal
Vicat Softening Temperature ISO 306/A50 89.0 �°C
Melting Temperature (DSC) DIN 53765 108 �°C
Peak Crystallization Temperature (DSC) DIN 53765 97.0 �°C
Heat of Fusion DIN 53765 110 J/g
Electrical
Volume Resistivity ASTM D257 8.5E+15 ohm â?¢cm
Dielectric Strength ASTM D149 30.0 kV/mm
Dielectric Constant (60Hz) ASTM D150 2.20 %
Dissipation Factor (60 Hz) ASTM D150 0.00050

LLDPE

Properties Test conditon Test method Test data Unit
Density 0.91
MFI 2
Drop impact strength ASTM D-1709 90 g
Elongation ,vertical/horizontal ASTM D-882 600/800 %
tensilestrength,thermal resistance ASTM D-1004 105/95 Kg/cm
elongation ASTM D-638 930 %
tensile strength ASTM D-638 180
tensile strength,vertical/horizontal ASTM D-882 380/350
Vicat softening point ASTM D-1525 103 C
melting point ASTM D-2117 126 C
Turbidity ASTM D-1009 12 %
45 glossness ASTM D-2457 75 %

Specification:
Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.

Application:

HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.


Application
Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.

Application: DS7601 application on PP, textiles, fabrics.

Composition: Polypropylene synthesis

Pipe grade

We Have Plenty Of Loads On Going 25kgs Packing Frm Dow Pe Loads As Above Mention,

Plz Interested Dm,

Loading Port Houston Tx Usa
Frm Dierect Our Facilities Houston Tx