Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Specification: Virgin. Type: Film grade, Injection molding grade, Blowing molding grade, extrusion grade,
High Density Polyethylene (HDPE): HDPE is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount of I±-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density.It has high temperatures, good rigidity,mechanical strength and anti-chemical corrosion. HDPE applications are including film, blow-molding, extrusion molding, injection molding, pipes, wire & cable and base material for producing chlorinated polyethylene. Product name HDPE Granules Type Plastic Raw Materials Granules Color Transparent and other colors Shape Pellet - Granules Application Packaging of all kinds of articles Density 0.924 g/cm3 MFR 0.6 - 0.8 G/10 Min Melting point 110~115 Processing 150~210
HDPE Feature Polymer; Thermoplastic; Polyethylene (PE); High Density (HDPE) The crystallinity is 80% to 90%, the softening point is 125 to 135'C, and the service temperature can reach 100'C; the hardness, tensile strength and creep are better than those of low-density polyethylene; abrasion resistance, electrical insulation, toughness and Good cold resistance; good chemical stability
Specifications: 1. HDPE 2. Transparent granule 3. We have all grades - Injection, Film and Moulding, all Density and Melt Flow Rate.
Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
High Density Polyethylene (HDPE): HDPE is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount of �±-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density.It has high temperatures, good rigidity,mechanical strength and anti-chemical corrosion. HDPE applications are including film, blow-molding, extrusion molding, injection molding, pipes, wire & cable and base material for producing chlorinated polyethylene.
HDPE (High Density Poly Ethylene) Origin: Petrochemical Plant Grade: Blown Film Grade Shape: Granules Loading Port: Jeddah, Saudi Arabia
Item Test Condition Test Method Value Unit MFR 190 C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C