Printing plate Thickness 0.15mm, 0.25mm, 0.30mm Alloy standard 1050 alloyh18 Maximum width 0.15mm/under 1020mm 0.25mm, 0.30mm/1100mm Grain ra 0.6-0.8um Coating weight 2.1-2.2 g/sq.M Anodized layer 2.5-3.2 g/sq.M Dots re production 2 -98 % Resolution power 8u~12u Sensitivity 140-200mj/ sq.M Running length 80000-100000printings Finall image color green Take specification 381mm*457mm*0.15mm as a example : A pallet`s weight is 891.2 kg The cumbic of it is :0.126 m3
Ps plate Thickness 0.15mm, 0.25mm, 0.30mm Alloy standard 1050 alloyh18 Maximum width 0.15mm/under 1020mm 0.25mm, 0.30mm/1100mm Grain ra 0.6-0.8um Coating weight 2.1-2.2 g/sq.M Anodized layer 2.5-3.2 g/sq.M Dots re production 2 -98 % Resolution power 8u~12u Sensitivity 140-200mj/ sq.M Running length 80000-100000printings Finall image color green 0.15mm 100 pieces/carton 0.25mm 50 pieces/carton 0.30mm 50 pieces/carton
140-200mj/ sq.M Exposure time :40 exposure unit (under 3kw gallium lodide lamps) 0.15mm 100 pieces/carton 0.25mm 50 pieces/carton 0.30mm 50 pieces/carton
Features: 1)highly press run and photosensitive material reduces exposure time 2)color changes after exposure, making it easy to check the image 3)reproduces original faithfully, results always show clear images 4)finished product performs well remaining clean and retaining moisture 5)quick ink-water balance Many kinds of dimensions
POSITIVE PRINTING PLATE Main Advantages : Photosensitive Coating Our photographic emulsion consists of imported photographic emulsion and resin, which can provides the plate with outstanding alkaline resistance, superior stability, high sensitive and increased adjusting flexibility when using. Due to our unique photographic emulsion, our plate has better resolving power. Vacuum ventilating layer With tiny ventilating grain layer on the surface, the vacuuming time during exposure can be greatly decreased, as well as preventing the proportion of tiny dots from exposuring to vague. Water Receptive Layer Excellent water reception capability speeds up the ink-water balance procedure and helps to reduce water absorption during printing process. Superior water retaining capability do effectively prevents non-image areas of the plate from scumming and avoids paper from distortion. Consequently, the printing quality improved. Multi Grain Layers Multi grain layers polish up water receptive property of the non-image areas on the plate. It increases the ink /water adjusting flexibility, make sure the developing performance of the tiny dots. It also strengthens the dotsâ??adsoption power to the coating layer, which can consequently extend the run-length of the plate. Anodic-Oxidized Layer A durable and strong oxidized surface formed after the anodic oxidation process on the aluminium material, which can help to prolong the run-length. This layer can also resists the corrosive effect done by the correction fluid
Ps printing plates Ps offset printing plates Please quote me the cif mumbai port rate per square meter for the 0.25 mm (actual 0.23 mm ) & 0.3 mm (actual 0.27 mm ) thickness plates. Size normally in demand are : Plate size: 0.510 * 0.640 = 0.32640 m2 Plate size: 0.540 * 0.660 = 0.35640 m2 Plate size: 0.576 * 0.720 = 0.41472 m2 Plate size: 0.560 * 0.800 = 0.44800 m2 Plate size: 0.576 * 0.840 = 0.48384 m2 Please quote me rate of both first grade & second grade ps plates. Quantity per month: 20000sqm Thanking you Prakash bansal
Printing plate
Positive-working offset plate with electrochemically grained anodized base light blue-green colored diazoic coating. Excellent quality light aluminum base. Unsurpassed technology matt surface treatment to improve film contact. Perform well on press and deliver excellent dot reproduction, with both AM/FM screening capabilities. Wide dampening latitude and good resistance to most pressroom. Excellent dot reproduction, water/ink balance and high printing quality. Aluminum: Thickness: 0.15 , 0.20 , 0.25 , 0.30 , 0.40 (mm) Maximum width: 1280mm Surface treatment: Electrochemical graining & anodizing Exposure: Light Source: Metal halogen lamp , ultraviolet light Exposure energy: 80 ( mj/c ) Dot reproductive range: 1~99 ( % ) ( at 200lpi ) Wavelength peak output: 360~420 ( nm ) (Peak : 405m) Vacuum contact larger: Micro Particles Recommended tonal wedge: UGRA Minimum clear step 2~3 Recommended micron lines: UGRA 8~10um Resolution power microlines200 LPI Print-out: Blackish blue to olive green Processing: Developer: MAX-6 Developer dilution: 1:6 (water) (ml) Processing temperature: 25í+ 2 (C) Processing time: 20~40 (secs) Replenishment Rate: 50~60 Photosensitive layer color: blue-green Working environment: Daylight Press room: Run length (Normal status) Unbaked: 200000 impressions Baked: above 1000000 impressions Static: 5~10 minutes at 200¬.
Live plate surface, Proper grain amount, Strong alkaline-proof ability Fine exposure &developing tolerance, Good plate life High color contrast