Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 Dark Drop Impact 105 g Brittle Temperature(F 50) -70 °C Vicat Softening Point 90°C Widely used for producing containers, such as, dispensing bottles, wash bottles, tubing, etc.
Request White masterbatches for: Blown film Blow molding Cast film Extrusion Injection molding Rotational molding Thermoforming Color White Ingredients Active: 25%, 50% , 60%, 70%, 75% Carrier: LDPE Dosage 0.5 to 8% depending on the end application Lifetime & Storage 12 months Storage in very humid areas or under direct sunlight for long periods should be avoided
WAX 2701; Flake; Packed in 25 kg composite bags Application: -Highly Effective Internal Lubricant for PE Base Masterbatch -Color/Black and White Masterbatch -Hotmelt Adhesive
WAX 2403; Flake/Pastille; Packed in 25 kg composite bags Application: -Highly Effective External Lubricant for PVC -PVC Base Color and Additive Masterbatch -PE and PP Base Masterbatch
Adding ratio: 5-50% (weight basis) MFI (g/10min) 3.5±1.0 Density (g/cm3) 1.65/1.70±0.05 Whiteness >90%, white granule, well plasticized pellet. Custom-making allowed. Transparent CaCO3 keeps optical property almost intact for translucent HDPE film. No powder/spot on plastic surface. Good dispersibility. Not block filter-sieve mesh. Optimize formula/process to achieve melt flowing dispersion, flexural tenacity and mechanical strength. 3. Packing and marking: – Masterbatch will be packed into PP/PE bag (25kg/bag) with label that following inquiry of customers. – Fullfilled bags will be put over pallets before loading into container